| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 |
| Physical | 比重 |
| ASTMD792 | 1.05 | g/cm3 |
| Physical | 密度 |
| ISO1183 | 1.05 | g/cm3 |
| Physical | 熔流率（熔體流動(dòng)速率）(220°C/10.0kg) |
| ASTMD1238 | 6.0 | g/10min |
| Physical | 溶化體積流率（MVR）(220°C/10.0kg) |
| ISO1133 | 6.00 | cm3/10min |
| Physical | 收縮率-流動(dòng) |
| ASTMD955 | 0.55 | % |
| Physical | 收縮率 |
| ISO294-4 | 0.40to0.70 | % |
| Physical | 吸水率(平衡,23°C,50%RH) |
| ISO62 | 0.25 | % |
| Mechanical | 拉伸模量 |
| ASTMD638 | 2800 | MPa |
| Mechanical | 拉伸模量 |
| ISO527-2 | 2700 | MPa |
| Mechanical | 抗張強(qiáng)度(屈服,23°C) |
| ASTMD638 | 58.0 | MPa |
| Mechanical | 拉伸應(yīng)力(屈服,23°C) |
| ISO527-2 | 58.0 | MPa |
| Mechanical | 拉伸應(yīng)變(屈服,23°C) |
| ISO527-2 | 3.1 | % |
| Mechanical | 伸長(zhǎng)率(斷裂) |
| ASTMD638 | 3.0 | % |
| Mechanical | 標(biāo)稱拉伸斷裂應(yīng)變(23°C) |
| ISO527-2 | 8.0 | % |
| Mechanical | 彎曲模量 |
| ASTMD790 | 2700 | MPa |
| Mechanical | 彎曲模量 |
| ISO178 | 2700 | MPa |
| Mechanical | 彎曲強(qiáng)度 |
| ASTMD790 | 88.3 | MPa |
| Mechanical | 彎曲應(yīng)力 |
| ISO178 | 81.0 | MPa |
| Impact | 簡(jiǎn)支梁缺口沖擊強(qiáng)度 | -30°C | ISO179 | 5.0 | kJ/m2 |
| Impact | 簡(jiǎn)支梁缺口沖擊強(qiáng)度 | 23°C | ISO179 | 12 | kJ/m2 |
| Impact | 簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 | -30°C | ISO179 | 80 | kJ/m2 |
| Impact | 簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 | 23°C | ISO179 | 140 | kJ/m2 |
| Impact | 懸壁梁缺口沖擊強(qiáng)度 | -30°C | ASTMD256 | 53 | J/m |
| Impact | 懸壁梁缺口沖擊強(qiáng)度 | 23°C | ASTMD256 | 100 | J/m |
| Hardness | 球壓硬度 |
| ISO2039-1 | 114 | MPa |
| Thermal | HeatDeflectionTemperature2(0.45MPa,Annealed) |
| ISO75-2/B | 110 | °C |
| Thermal | 熱變形溫度2(1.8MPa,退火) |
| ISO75-2/A | 102 | °C |
| Thermal | 維卡軟化溫度 | -- | ISO306/A50 | 118 | °C |
| Thermal | 維卡軟化溫度 | -- | ISO306/B50 | 112 | °C |
| Thermal | 線形熱膨脹系數(shù)-流動(dòng) |
| ISO11359-2 | 9.0E-5 | cm/cm/°C |
| Thermal | 導(dǎo)熱系數(shù) |
| DIN52612 | 0.17 | W/m/K |
| Thermal | *使用溫度 |
|
| 90 | °C |
| Thermal | HeatDeflectionTemperature2(0.45MPa,Annealed) |
| ISO75-2/B | 110 | °C |
| Thermal | 熱變形溫度2(1.8MPa,退火) |
| ISO75-2/A | 102 | °C |
| Thermal | 維卡軟化溫度 | -- | ISO306/A50 | 118 | °C |
| Thermal | 維卡軟化溫度 | -- | ISO306/B50 | 112 | °C |
| Thermal | 線形熱膨脹系數(shù)-流動(dòng) |
| ISO11359-2 | 9.0E-5 | cm/cm/°C |
| Thermal | 導(dǎo)熱系數(shù) |
| DIN52612 | 0.17 | W/m/K |
| Thermal | *使用溫度 |
|
| 90 | °C |
| Electrical | 體積電阻率 |
| ASTMD257 | >1.0E+15 | ohms·cm |
| Electrical | 體積電阻率 |
| IEC60093 | 1.0E+15 | ohms·cm |
| Electrical | ElectricStrength(1.50mm) |
| IEC60243-1 | 41 | kV/mm |
| Electrical | 漏電起痕指數(shù) |
| IEC60112 | 600 | V |