PA6 1011G-45 日本東麗
生產(chǎn)企業(yè)：日本東麗
規(guī)格用途
| 規(guī)格級(jí)別 | 其它 其它 注塑 | 外觀顏色 | |
| 該料用途 | |||
| 備注說明 | |||
技術(shù)參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | 23℃，24hr | ASTM D-570 | Dry｜1.9%Water0.9｜- | % |
| 吸水率 | 23℃ | ASTM D-570 | Dry｜1.9%Water5.3｜- | % | |
| 物理性能 | 比重 | ASTM D-792 | Dry｜1.9%Water1.50｜- | ||
| 機(jī)械性能 | 斷裂伸長率 | -40℃ | ASTM D-638 | Dry｜1.9%Water4.5｜4.5 | % |
| 彎曲模量 | 23℃ | ASTM D-790 | Dry｜1.9%Water12.0｜7.1 | GPa | |
| IZOD缺口沖擊強(qiáng)度 | -40℃ | ASTM D-256 | Dry｜1.9%Water125｜145 | J/m | |
| 彎曲模量 | 80℃ | ASTM D-790 | Dry｜1.9%Water6.2｜4.4 | GPa | |
| 拉伸屈服強(qiáng)度 | 23℃ | ASTM D-638 | Dry｜1.9%Water205｜130 | MPa | |
| 彎曲模量 | -40℃ | ASTM D-790 | Dry｜1.9%Water14.0｜12.5 | GPa | |
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790 | Dry｜1.9%Water290｜180 | MPa | |
| 斷裂伸長率 | 23℃ | ASTM D-638 | Dry｜1.9%Water5.0｜5.0 | % | |
| 拉伸屈服強(qiáng)度 | 80℃ | ASTM D-638 | Dry｜1.9%Water120｜85 | MPa | |
| IZOD無缺口沖擊強(qiáng)度 | 23℃ | ASTM D-256 | Dry｜1.9%Water100｜120 | KJ/m2 | |
| 彎曲強(qiáng)度 | -40℃ | ASTM D-790 | Dry｜1.9%Water330｜280 | MPa | |
| IZOD缺口沖擊強(qiáng)度 | 23℃ | ASTM D-256 | Dry｜1.9%Water155｜195 | J/m | |
| 抗壓強(qiáng)度 | -40℃ | ASTM D-695 | Dry｜1.9%Water260｜220 | MPa | |
| 抗壓強(qiáng)度 | 23℃ | ASTM D-695 | Dry｜1.9%Water190｜120 | MPa | |
| 抗壓強(qiáng)度 | 80℃ | ASTM D-695 | Dry｜1.9%Water100｜70 | MPa | |
| 剪切強(qiáng)度 | 23℃ | ASTM D-732 | Dry｜1.9%Water95｜75 | MPa | |
| 斷裂伸長率 | 80℃ | ASTM D-638 | Dry｜1.9%Water8.0｜8.0 | % | |
| 彎曲強(qiáng)度 | 80℃ | ASTM D-790 | Dry｜1.9%Water160｜110 | MPa | |
| 洛氏硬度 | 23℃ | ASTM D-785 | Dry｜1.9%WaterR121,M95｜- | R Scale | |
| IZOD無缺口沖擊強(qiáng)度 | -40℃ | ASTM D-256 | Dry｜1.9%Water90｜95 | KJ/m2 | |
| 拉伸屈服強(qiáng)度 | -40℃ | ASTM D-638 | Dry｜1.9%Water290｜250 | MPa | |
| 熱性能 | 熱導(dǎo)率 | Dry｜1.9%Water0.40｜- | W/m℃ | ||
| 線性熱膨脹系數(shù) | ASTM D-696 | Dry｜1.9%Water2-3｜- | 10-5/℃ | ||
| 比熱 | Dry｜1.9%Water1.4｜- | J/p℃ | |||
| 熔點(diǎn) | DSC | Dry｜1.9%Water225｜- | ℃ | ||
| 熱變形溫度 | 0.46MPa | ASTM D-648 | Dry｜1.9%Water225｜- | ℃ | |
| 熱變形溫度 | 1.86MPa | ASTM D-648 | Dry｜1.9%Water215｜- | ℃ | |
| 其它性能 | 加強(qiáng)材料 | Dry｜1.9%Water45｜45 | WT% | ||
PA6 1011G-45 日本東麗